合金牌號 | 鑄造方法 | 力學(xué)性能,不低于 | |||
σb/MPa(kgf/mm2) | σ0.2/MPa(kgf/mm2) | δ5(%) | 硬度HBW | ||
ZCuAl8Mn13Fe3 | S | 600(61.2) | 270(27.5) | 15 | 1570 |
J | 650(66.3) | 280(28.6) | 10 | 1665 | |
ZCuAl8Mn13Fe3Ni2 | S | 645(65.8) | 280(28.6) | 20 | 1570 |
J | 670(68.3) | 310(31.6) | 18 | 1665 | |
ZCuAl9Mn2 | S | 390(39.8) | 20 | 835 | |
J | 440(44.9) | 20 | 930 | ||
ZCuAl9Fe4Ni4Mn2 | S | 630(64.3) | 250(25.5) | 16 | 1570 |
ZCuAl10Fe3 | S | 490(50.0) | 180(18.4) | 13 | 980 |
J | 540(55.1) | 200(20.4) | 15 | 1080 | |
Li、La | 540(55.1) | 200(20.4) | 15 | 1080 | |
ZCuAl10Fe3Mn2 | S | 490(50.0) | 15 | 1080 | |
J | 540(55.1) | 20 | 1175 |